NACE MR0175 / ISO 15156 for Corrosion Resistant Alloy By yaang.com

Written by
NACE MR0175 / ISO 15156 for Corrosion Resistant Alloy By yaang.com

NACE MR 0175/ISO 15156 is a Materials Standard issued by the National Association of Corrosion Engineers.
It is originally a US standard intended to assess the suitability of materials for oilfield equipment where sulphide (sulfide) stress corrosion cracking may be a risk in hydrogen sulphide (sour) environments. However, the world standards body ISO has issued it under its own “brand”. The latest edition includes technical corrigenda from 2005.

The standard specifies the types of corrosion resistant materials including stainless steel that can be used in specific oilfield environments and places limits on the hardness of the material. This applies both to parent and weld material. The maximum hardness is usually defined in terms of the Rockwell ‘C’ scale.
No conversion to other hardness scale is given in MR 0175 which presents one problem as softened stainless steel hardness are measured using either the Rockwell ‘B’, Vickers or Brinell scales. Approximate conversions are available.

Summary of MR 0175 Requirements

A wide range of materials is covered by the standard including most types (families) of stainless steel. The table below shows some of these grades. However, this summary is intended to only give a general idea of this complex standard and is not a substitute for the original document.

Stainless Steel Type Grades Included                                  Comments                                                                                         
Ferritic Stainless Steel 405,430, 409, 434, 436, 442, 444, 445, 446, 447, 448 Hardness up  to 22 HRC
Martensitic Stainless Steel 410, 420 Hardness up to 22 HRC
Martensitic Stainless Steel F6NM Hardness up to 23 HRC
Martensitic Stainless Steel S41425 Hardness up to 28 HRC
Austenitic Stainless Steel 201, 202, 302, 304304L, 305, 309310, 316, 316L, 317321347, S31254(254SMO), N08904(904L), N08926(1925hMo) Solution annealed, no cold work to enhance properties, hardness up to 22 HRC
Austenitic Stainless Steel S20910 Hardness up to 35 HRC
Duplex Stainless Steel  S31803 (1.4462), S32520 (UR 52N+),S32750 (2507), S32760 (Zeron 100), S32550(Ferralium 255) PREN >30 solution annealed condition, ferrite content 35% to 65%, or 30 to 70% in welds. Note that the general restriction of 28 HRC in previous editions is not found in this latest edition of the standard. There is a specific restriction on HIP’d S31803 to 25HRC. For some applications cold worked material is allowed up to 36HRC

Precipitation Hardening

17-4 PH 33 HRC Age hardening at 620 deg C
Precipitation Hardening 
S45000 31 HRC Age hardening at 620 deg C
Precipitation Hardening S66286 35 HRC

Free machining grades such as the 303 and 416 types are excluded from of NACE MR 0175/ISO 15156

Source: Zhejiang Yaang Pipe Industry Co., Limited (www.yaang.com)