Martensitic Stainless Steel 410

Subcategory: Metal; Stainless Steel; T 400 Series Stainless Steel; Martensitic

Component Wt. %
C Max 0.15
Cr 11.5 – 13.5
Mn Max 1
Ni Max 0.5
P Max 0.04
S Max 0.03
Si Max 1

Characteristics: superior wear resistance, hardenable, excellent corrosion resistance.

Applications: cutlery, dental and surgical instruments, nozzles, valve parts, 

hardened steel ball and seats for oil well pumps, separating screens and strainers, 

springs, shears, and wear surfaces.

Information provided by Zhejiang Yaang Pipe Industry Co., Limited

Physical Properties Metric English Comments
Density 7.64 g/cc 0.276 lb/in³
Specific Gravity 7.65 g/cc 0.276 lb/in³
Mechanical Properties
Hardness, Rockwell B 82 82
Hardness, Rockwell B 98 98 Hardened+Tempered 1200°F
Hardness, Rockwell C -7 -7 Hardening Response
Hardness, Rockwell C 35 35 Hardened+Tempered 1000°F
Hardness, Rockwell C 40 40 Hardened+Tempered 550°F
Hardness, Rockwell C 40 40 Hardened+Tempered 600°F
Hardness, Rockwell C 41 41 Hardened+Tempered 800°F
Hardness, Rockwell C 41 41 Hardened+Tempered 900°F
Hardness, Rockwell C 43 43 Hardened+Tempered 400°F
Tensile Strength, Ultimate 1063 MPa 154000 psi Hardened 1800°F, Tempered 1000°F
Tensile Strength, Ultimate 1283 MPa 186000 psi Hardened 1800°F, Tempered 600°F
Tensile Strength, Ultimate 1289 MPa 187000 psi Hardened 1800°F, Tempered 550°F
Tensile Strength, Ultimate 1298 MPa 188000 psi Hardened 1800°F, Tempered 900°F
Tensile Strength, Ultimate 1300 MPa 189000 psi Hardened 1800°F, Tempered 800°F
Tensile Strength, Ultimate 1399 MPa 203000 psi Hardened 1800°F, Tempered 400°F
Tensile Strength, Ultimate 510 MPa 74000 psi Annealed
Tensile Strength, Ultimate 767 MPa 111000 psi Hardened 1800°F, Tempered 1200°F
Tensile Strength, Yield 1022 MPa 148000 psi Hardened 1800°F, Tempered 550°F
Tensile Strength, Yield 1026 MPa 149000 psi Hardened 1800°F, Tempered 600°F
Tensile Strength, Yield 1076 MPa 156000 psi Hardened 1800°F, Tempered 400°F
Tensile Strength, Yield 290 MPa 42100 psi 0.2% offset, Annealed
Tensile Strength, Yield 589 MPa 85400 psi Hardened 1800°F, Tempered 1200°F
Tensile Strength, Yield 845 MPa 123000 psi Hardened 1800°F, Tempered 900°F
Tensile Strength, Yield 882 MPa 128000 psi Hardened 1800°F, Tempered 1000°F
Tensile Strength, Yield 916 MPa 133000 psi Hardened 1800°F, Tempered 800°F
Elongation at Break 34 % 34 % Annealed
Electrical Properties
Electrical Resistivity 5.6e-005 ohm-cm 5.6e-005 ohm-cm
CTE, linear 20°C 10.5 µm/m-°C 5.83 µin/in-°F 20°C-200°C
CTE, linear 500°C 11.6 µm/m-°C 6.44 µin/in-°F 20°C-600°C
Heat Capacity 0.46 J/g-°C 0.11 BTU/lb-°F
Thermal Conductivity 24.9 W/m-K 173 BTU-in/hr-ft²-°F 100°C
Processing Properties
Melt Temperature 1482 – 1532 °C 2700 – 2790 °F
Descriptive Properties
Corrosion Rate mils per year 0.079 (5% Acetic Acid at 49°C) Hardened martensitic grades were tested after tempering at 204°C.
Corrosion Rate mils per year 0.062 (5% Phosphoric Acid at 49°C) Hardened martensitic grades were tested after tempering at 204°C
Pitting Potential, Volts vs Sat. Calomel Electrode 0.502 100 ppm Chloride solution at 24°C, pH5. Samples had ground surface. Hardened martensitic grades were tested after tempering at 204°C.

Established in 2008, Zhejiang Yaang Pipe Industry Co., Limited is a professional organizer and one-stop-shop supplier for steel piping system products, including stainless steel pipe and tube, forged flange and fittings, butt-welding pipe fittings, elbow, tee, reducer, stub end, gaskets, fasteners, valves, Sanitary Services etc. in China. We have devoted to providing the best solutions of steel materials and industrial equipment for our respected customers.

This information is provided by yaang.com

Article Categories:
Stainless Steel

Leave a Comment

Your email address will not be published. Required fields are marked *